Düşük Karbonlu Çeliğin Korozyon Davranışına Hekzametilen Tetra Amin’in Etkisi

Abstract

In this study, the inhibition effect of hexamethylene tetramin (HMTA) on low carbon steel corrosion behavior in acidic environment is investigated. The electrochemical techniques and quantum chemical calculations were obtained. The results showed that; inhibition efficiencies increase with increasing concentration of HMTA. The inhibition efficiency is 93,6% in 10 mM HMTA containing 0,1 M HCl solution. The high inhibition efficiency of HMTA is attributed to the high value of EHOMO (-6.203 eV) and low value of ELUMO (-0.346 eV). The adsorption of HMTA on mild steel was found to fit to Langmuir adsorption isotherm. The inhibition efficiency of HMTA was discussed in terms of adsorption of inhibitor molecules on the metal surface and a protective film formation.Bu çalışmada düşük karbonlu çeliğin (DKÇ) asidik ortamındaki korozyon davranışına hekzametilen tetra âmin’in (HMTA) inhibitör etkisi araştırılmıştır. Elektrokimyasal teknikler ve kuantum kimyasal hesaplamalar uygulanmıştır. Elde edilen sonuçlara göre; HMTA’nın inhibisyon etkinliği artan HMTA derişimi ile artış göstermiştir. 10 mM HMTA içeren 0,1 M HCl çözeltisinde inhibisyon etkinliği %93,6 olarak tespit edilmiştir. Yüksek inhibisyon etkinliği, teorik olarak belirlenen yüksek HOMO (en yüksek enerjili dolu moleküler orbital enerjisi) enerjisi (-6,203 eV) ve düşük LUMO (en düşük enerjili boş moleküler orbital enerjisi) enerjisi (-0,346 eV) ile ilişkilendirilmiştir. HMTA’in yumuşak çelik yüzeyine adsorpsiyonunun Langmuir adsorpsiyon izotermine uyduğu tespit edilmiştir. HTMA’in inhibisyon etkinliği, inhibitör moleküllerinin metal yüzeyine adsorplanarak koruyucu bir film oluşturması ile açıklanabilir.